B27R095 Grain Oriented Electrical Steel

B27R095 Grain Oriented Electrical Steel

Its unique properties make it an ideal material for use in applications that require high efficiency, low core loss, and high magnetic permeability.

B27R095 steel Mechanical Properties

Grade	tensile strength L（N/mm2）	Yield Strength L（N/mm2）	Elongation L（%）	Hardness HV1	Bending frequency (times)	Stacking factor（%）
B27R095	355	330	10	200	18	97.5

NOTE:. A detector according to GB / t228-2002, GB / T 19289-2003
b. above are typical values only for reference does not guarantee
c. L direction refers to the rolling direction

B27R095 steel plate electromagnetic performance standards

Grade	Nominal thickness（mm）	Theoretical density（kg/dm3）	Maximum core loss P17/50 (W/kg)	The minimum magnetic induction B8 （T）
B27R095	0.27	7.65	0.95	1.87

NOTE:. A detector according to GB / T 3655-2008 (G-series and P-series), GB / T3789-2008 (R Series)
b . G-series and P-series samples were rolling direction, and incubated for 2 hours at 800 ℃ magnetically eliminate stress after annealing treatment can be tested
c . P17/50 represents the maximum magnetic flux density of 1.7T, a frequency of 50Hz, the unit kg sample of core loss.
d . B50 represents the magnetic field intensity corresponding to the intensity of the magnetic induction 5000A / m when.